| 产品特性：耐高温尼龙 | 是否进口：否 | 产地：泰科纳 |
| 厂家(产地)：泰科纳 | 牌号：GF20-02P11 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PA66 | 加工级别：注塑级、 挤出级 |
| 特性级别：增韧级、 增强级、 透明级、 热稳定性、 耐高温、 耐低温、 抗紫外线、 标准级、 耐磨、 耐候、 高强度 | 用途级别：通用级、 填充级、 汽车部件、 管材级、 运动器材、 瓶盖专用料、 流延膜专用料、 家电部件、 电线电缆级、 电动工具配件 | 品牌：泰科纳 |
| 产品规格：pa66 |
特点：泰科纳 PA66 GF20-02P11/12 是一个含20%长玻璃纤维增强、高刚性、高强度、抗撞击性良好、良好的抗蠕变性、耐低温撞击
Celstran PA66 GF20-02P11/12
CELSTRAN PA66-GF20-02P11/12 | PA66 | Glass Reinforced
Description
Nylon 66 reinforced by 20 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.
Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the warpage.
Complex parts can be manufactured with high reproducibility by injection molding.
Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.
ISO Data | Physical properties | Value | Unit | Test Standard |
Phys | Density | 1300 | kg/m? | ISO 1183 |
Mech | Tensile modulus (1mm/min) | 8300 | MPa | ISO 527-2/1A |
Tensile modulus (80℃) | 4970 | MPa | ISO 527-2/1A | |
Tensile strength (80℃) | 103 | MPa | ISO 527-2/1A | |
Tensile stress at break (5mm/min) | 125 | MPa | ISO 527-2/1A | |
Tensile strain at break (5mm/min) | 1.6 | % | ISO 527-2/1A | |
Elongation at break (80℃) | 2.6 | % | ISO 527-2/1A | |
Flexural modulus (23℃) | 7100 | MPa | ISO 178 | |
Flexural modulus (80℃) | 4400 | MPa | ISO 178 | |
Flexural strength (23℃) | 190 | MPa | ISO 178 | |
Flexural strength (80℃) | 175 | MPa | ISO 178 | |
Charpy impact strength @ 23℃ | 41 | kJ/m? | ISO 179/1eU | |
Charpy impact strength @ -30℃ | 52 | kJ/m? | ISO 179/1eU | |
Charpy notched impact strength @ 23℃ | 24 | kJ/m? | ISO 179/1eA | |
Charpy notched impact strength @ -30℃ | 27 | kJ/m? | ISO 179/1eA | |
Notched impact strength (Izod) @ 23℃ | 19 | kJ/m? | ISO 180/1A | |
Notched impact strength (Izod) @-30℃ | 21 | kJ/m? | ISO 180/1A | |
Therm | Melting temperature (10℃/min) | 260 | ℃ | ISO 11357-1,-2,-3 |
DTUL @ 1.8 MPa | 260 | ℃ | ISO 75-1/-2 | |
DTUL @ 8.0 MPa | 238 | ℃ | ISO 75-1/-2 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
Drying time (h)：2 - 4
Drying temperature (℃)：70 - 80